Engineering materials are typically tested in a uniaxial state of stress as the tests are straightforward; however, many materials exhibit different behavior when loaded under different states of stress. It is therefore important to perform tests beyond the standard uniaxial tension/compression tests to capture fully a material’s response. Biaxial loading is one such state of stress that may be encountered as a component bulges due to internal pressure, for instance. 

The small punch test, shown in the image below, is designed to characterize a material’s behavior under biaxial stress and is based on ASTM F2183. A punch with a 2.54mm diameter spherical tip is pressed into a clamped thin cylindrical specimen. Punch load and displacement are measured until specimen failure. The results from this test are typically used to characterize the biaxial stress-strain response of a material and to validate a material model developed solely with uniaxial data.

Small punch apparatus and tested specimen


More Information

For more information or a customized quotation, please click the button below:


Call Us
Email
Print

To contact Veryst, please call:

+1-781-433-0433

Close